| 鉻鉬合金鋼標(biāo)準(zhǔn)規(guī)范 Standard Specification for Cr-Mo Alloy Steel | ||||||||
| 參考標(biāo)準(zhǔn) Reference Standard | 化學(xué)成分 Nominal Chemical Composition (W%) | |||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | |
| AS 2074/L2A | 0.45-0.55 | ≤0.75 | 0.50-1.00 | ≤0.04 | ≤0.04 | - | 0.80-1.20 | - |
| AS 2074/L2B | 0.55-0.65 | ≤0.75 | 0.50-1.00 | ≤0.04 | ≤0.04 | - | 0.80-1.50 | 0.2-0.4 |
| AS 2074/L2C | 0.70-0.90 | ≤0.75 | 0.50-1.20 | ≤0.04 | ≤0.04 | - | 1.30-2.40 | 0.2-0.4 |
| ZG42Cr2Si2MnMo | 0.38-0.48 | 1.5-1.8 | 0.8-1.2 | ≤0.04 | ≤0.04 | - | 1.8-2.2 | 0.2-0.6 |
| ZG45Cr2Mo | 0.40-0.48 | 0.8-1.2 | 0.4-1.0 | ≤0.04 | ≤0.04 | ≤0.5 | 1.7-2.0 | 0.8-1.2 |
| ZG30Cr5Mo | 0.25-0.35 | 0.4-1.0 | 0.5-1.2 | ≤0.04 | ≤0.04 | ≤0.5 | 4.0-6.0 | 0.2-0.8 |
| ZG40Cr5Mo(FED4A) | 0.35-0.45 | 0.4-1.0 | 0.5-1.2 | ≤0.04 | ≤0.04 | ≤0.5 | 4.0-6.0 | 0.2-0.8 |
| ZG50Cr5Mo | 0.45-0.55 | 0.4-1.0 | 0.5-1.2 | ≤0.04 | ≤0.04 | ≤0.5 | 4.0-6.0 | 0.2-0.8 |
| ZG60Cr5Mo | 0.55-0.65 | 0.4-1.0 | 0.5-1.2 | ≤0.04 | ≤0.04 | ≤0.5 | 4.0-6.0 | 0.2-0.8 |
| FMU-29 | 0.25-0.45 | 0.3-1.0 | 0.6-1.5 | ≤0.04 | ≤0.04 | - | 6.0-8.0 | 0.2-0.4 |
| FMU-11 | 0.90-1.30 | 0.3-1.0 | 0.6-1.5 | ≤0.04 | ≤0.04 | - | 11.0-13.0 | 0.3-0.5 |
| FED-13 | 0.80-1.30 | 0.4-1.2 | 0.8-1.5 | ≤0.04 | ≤0.04 | - | 11.0-13.0 | 0.4-0.8 |
| FED-14 | 1.60-2.00 | 0.4-1.2 | 0.8-1.5 | ≤0.04 | ≤0.04 | - | 11.0-13.0 | 0.6-1.0 |
性能 · 特點(diǎn)
產(chǎn)品性能
材質(zhì)：鉻鉬合金鋼
硬度：≥HB310
沖擊韌性值：AK≥60J(常溫，無(wú)缺口)
產(chǎn)品特點(diǎn)
球磨機(jī)襯板用于保護(hù)磨機(jī)筒體免受研磨體和礦石的直接沖擊和摩擦。 同時(shí)，可以使用不同的襯板來(lái)調(diào)節(jié)研磨體的運(yùn)動(dòng)狀態(tài)，從而增強(qiáng)研磨體對(duì)物料的研磨效果，提高磨機(jī)的研磨效率，增加產(chǎn)量，減少研磨量和金屬消耗。
提供經(jīng)過(guò)適當(dāng)熱處理工藝的合金鋼半自磨機(jī)襯板鑄件。
按國(guó)際標(biāo)準(zhǔn)生產(chǎn)高品質(zhì)的水泥磨襯板：GB/T26651,GB/T8263-1999,AS2074, AS2027, DIN 1695, AISI,ASTM,JIS G 5153,NF A32401,BS4844。
根據(jù)具體工況為您選擇合適的礦山磨材質(zhì)，提高磨機(jī)的生產(chǎn)效率，減少襯板和磨球的磨耗。